GH3536 (GH536) nickel-based superalloy overview

GH3536 is a nickel-based superalloy with high iron content mainly solid-solution strengthened with chromium and molybdenum. It has good resistance to corrosion and corrosion resistance. It has moderate durability and creep strength below 900 ℃. Good hot workability and weldability. Used in the manufacture of aero engine combustion chamber components and other high-temperature components, long-term use below 900 ℃, short-term working temperature can reach 1080 ℃. The main varieties supplied are plates, strips, pipes, bars, forgings, rings and precision castings.

 

GH3536 (GH536) nickel-based superalloy chemical composition

C	Cr	Ni	Ti	Mo	Al	W	Fe
0.05 0.15	20.50 23.00	margin	≤ 0.15	8.00  10.00	≤ 0.50	0.20 1.00	17.00 20.00
B	Cu	Co	Mn	Si	P	S
≤ 0.010	≤ 0.50	0.50 2.50	≤ 1.00	≤ 1.00	≤ 0.025	≤ 0.015

GH3536 (GH536) nickel-based superalloy similar grades

GH3536 GH536, UNS NO6002, HastelloyX (USA), NC22FeD (France), NiCr22FeMo (Germany), Nimonic PE13 (UK)

 

GH3536 (GH536) nickel-based superalloy heat treatment system

Plates and tubes: 1130 ～ 1170 ℃, fast air cooling or water cooling; bar and ring inspection samples: 1175 ℃ ± 15 ℃, air cooling or faster cooling; strip: 1065 ～ 1105 ℃, rapid cooling.

 

GH3536 (GH536) nickel-based superalloy variety specifications and supply status

Supply δ0.5 ～ 4.0mm sheet, δ0.05 ～ 0.8mm strip, outer diameter 4 ～ 20mm, wall thickness 1.0 ～ 2.0mm pipe, diameter 0.2 ～ 10.0mm welding wire, diameter ≤300mm bar and Rings of various diameters and wall thicknesses and precision castings of different shapes and sizes. Plates, strips and pipes are supplied after solution treatment and pickling, and the strips can also be supplied in cold rolled state; the welding wire is delivered in a hard state, semi-hard state, solid solution plus pickling, and bright solution treatment. , Can also be delivered straight; bars and rings are delivered without heat treatment. Precision castings are supplied in the casting state.

GH3536 (GH536) nickel-based superalloy melting and casting process

Adopt electric arc furnace plus electroslag or non-vacuum induction furnace plus electroslag remelting process. The casting is produced by remelting the master alloy in an induction furnace and pouring it into the heated mold shell. The pouring speed is better.

 

GH3536 (GH536) nickel-based superalloy application profile and special requirements

GH3536 nickel-based deformed superalloy is used to manufacture the combustion chamber components and other high-temperature components of aircraft engines. It can be used for a long time under 900 ℃, and the short-term working temperature can reach 1080 ℃. It has good resistance to corrosion and corrosion resistance. It has moderate endurance and creep strength below 900 ℃. It has good formability in cold and hot processing and good welding performance.