XM-9 precipitation hardening stainless steel S36200

XM-9 (S36200) precipitation hardening stainless steel characteristics:

Compared with cobalt-containing and high-nickel alloys, xm-9 stainless steel can achieve corrosion resistance and wear resistance at extremely low cost. Its overall corrosion resistance is better than Type 304 in most media. In xm-9 stainless steel, resistance to chloride pitting is better than type 316. The yield strength at room temperature is almost twice that of 304 and 316.

xm-9 stainless steel has excellent high temperature oxidation resistance and low temperature impact resistance.

 

XM-9 (S36200) precipitation hardening stainless steel chemical composition:

C	Si	Mn	P	S	Cr	Ni	Ti	Al	Mo
≤ 0.05	≤ 0.30	≤ 0.50	≤ 0.030	≤ 0.030	14.00 14.50	6.25 7.00	0.60 0.90	≤ 0.10	≤ 0.30

 

XM-9 (S36200) precipitation hardening stainless steel physical properties:

Density8.0g / cm3

Melting point

 

XM-9 (S36200) Minimum value of solid solution state of mechanical properties of precipitation hardening stainless steel:

Tensile strength Rm N / mm2 690

Yield strength RP0.2 N / mm2 380

Elongation A5% 35

Brinell hardness HB≤241